Brazing alloy Composition % Melting range Operating Temp. Density Tensile strenght International standard corrispondences Recommended Flux
  Ag Cu Zn Sn ° C ° C g / cm 3 N / mm 2 DIN 8513 AWS A 5.8 BS 1845 NFA 81 - 362 ISO 3677 ISO 3677
Ag 20 20 44 36   690 - 810 810 8,7 330 L - Ag 20     20 A1 B Cu 44 - Zn Ag 690-810 HARD
Ag 30 Sn 30 36 32 2 680 - 765 750 8,9 460 L - Ag 30 Sn   AG 21   B Cu 36 Zn - Ag Sn 680-765 N° 2
Ag 34 Sn 34 36 27 3 630 - 730 710 9 420 L - Ag 34 Sn       B Cu 36 Ag Zn - Sn 630-730 N° 3
Ag 40 Sn 40 30 28 2 640 - 700 690 9,1 430 L - Ag 40 Sn B Ag 28 Ag 20   B Ag 40 Cu Zn - Sn 640-700 N° 3
Ag 45 Sn 45 27 25 3 640 - 680 670 9,2 350 L - Ag 45 Sn B Ag 36     B Ag 45 Cu Zn - Sn 640-680 N° 3
Ag 55 Sn 55 21 22 2 620 - 660 650 9,4 390 L - Ag 55 Sn   Ag 14   B Ag 55 Zn Cu - Sn 620-660 N° 1

Copper - Phosphorus - Silver - Tin Alloys

Brazing alloy Composition % Melting range Operating Temp. Density Tensile strenght International standard corrispondences Recommended Flux
  Ag Cu P ° C ° C g / cm 3 N / mm 2 DIN 8513 AWS A 5.8 BS 1845 NFA 81 - 362 ISO 3677 ISO 3677
Cu P 7   93 7 710 - 820 720 8,1 250 L - Cu P 7 B Cup - 2 CP 3 07B1 B Cu 93 P 710 - 820 N° 2
Cu P Ag 2 2 91,8 6,2 645 - 800 710 8,1 250 L - Ag 2 P B Cup - 6 CP 2 06B1 B Cu 92 P Ag 645 - 800 N° 2
Cu P Ag 5 5 88,8 6,2 645 - 810 710 8,2 250 L -Ag 5 P B Cup - 3 CP 4 06B2 B Cu 89 P Ag 645 - 780 N° 2
Cu P Ag 15 15 80,3 4,7 645 - 800 710 8,4 250     CP 1   B Cu 80 Ag P 645 - 800 N° 2
Cu P Ag 18 18 75 7 645 - 670 660 8,6 250       07B4 B Cu 75 Ag P 645 - 670 N° 1